PEEK Cable

1. Introduction to PEEK (polyetheretherketone) cable

PEEK insulated wires have outstanding high and low temperature resistance, flame retardancy, radiation resistance and good mechanical properties, making them suitable for use as ultra-high temperature conductors in the aviation industry; they can be used as winding wires and connecting wires for submersible pump motors in the petroleum industry, and as winding coils for nuclear island drive mechanisms in atomic power plants for long-term use under irradiation conditions; PEEK insulated wires have excellent properties such as seawater resistance, light weight, small size and flame retardancy, making them suitable for use in ships; they are used in high-speed traction locomotives.

1. Halogen-free performance

PEEK material molecules do not contain halogen atoms, and do not produce acidic and toxic gases after combustion. It complies with EU RoSH and other environmental protection requirements and is an environmentally friendly material.

2. Volume resistance

In a wide temperature range, ordinary PEEK polymer can still maintain a very high volume resistivity value. At 23°C, the volume resistivity of PEEK is above 6 × 10 ¹³ Ωm; at 140°C, its volume resistivity is above 8 × 10 ¹² Ωm; and at 200°C, its volume resistivity is above 6 × 10 ⁹ Ωm, still having excellent insulation properties.

3. Surface resistance

The surface resistivity of PEEK at 25°C and 50% humidity reaches 2.0 × 10 ¹⁶ Ω, which is superior to fluoroplastics, polyamide, polyimide and other plastics.

4. Dielectric constant and dielectric loss factor

The dielectric constant of PEEK5600G is only 3.2, which is slightly higher than polyethylene (PE) and fluoroplastics, but much lower than polyvinyl chloride (PVC). In the frequency range of 10 ⁹ Hz, ordinary PEEK polymer has good electrical properties. Many of the electrical properties of this material are in line with the typical properties of thermoplastic materials, and PEEK polymer also maintains these excellent insulation properties over a very wide temperature and frequency range. Below 140°C, the tanδ loss of PEEK material is small. PPS is polyphenylene sulfide, PES is polyethersulfone, PC is polycarbonate, and PSU is bisphenol A type polysulfone.

5. Heat resistance

PEEK polymer has a glass transition temperature of 143℃. Since it is a semi-crystalline thermoplastic material, it can still maintain excellent mechanical properties near the melting point of 343℃. Its fatigue resistance and creep resistance are higher than those of thermoplastics.

6. Flame retardancy

PEEK is self-extinguishing. Without adding flame retardant, the UL standard reaches 94V-1 (thickness 0.3 mm), 94V-0 (thickness 1.5 mm), and 94V-5 (thickness 3.2 mm). In addition, the amount of smoke generated during combustion is very small.

7. Environmental resistance

PEEK only dissolves in concentrated sulfuric acid and has good chemical resistance, especially in terms of acid and alkali resistance at high temperature, which is much better than polyimide. At the same time, PEEK has a very low water absorption rate, and the saturated water absorption rate at 23℃ is only 0.5%. It also has good hot water resistance and can be used in pressurized hot water or steam at 300℃.

8. Radiation resistance

It has a strong ability to resist γ-ray radiation, which exceeds the radiation resistance of polystyrene among general resins. It can be made into wires that can still maintain good insulation performance when the γ-ray radiation dose reaches 850KGy.

2. PEEK cable specifications

Outer diameter 3mm Inner diameter 2.5 Outer diameter 3mm Inner diameter 2.6 Outer diameter 3mm Inner diameter 2mm (can be customized)

The PEEK cable wire extrusion production equipment introduced by the company can extrude PEEK cables of various specifications according to customer needs. Welcome to consult and purchase!

3. Process Capability

1. Applicable conductors: single core, composite core wire, braided core wire, and sheathed wire can also be produced;

2. Applicable conductor diameter: 0.50mm2~6.0mm2 copper wire or core wire sheath extrusion, coating thickness: 0.05~0.30mm;

3. Coating material: PEEK polyetheretherketone material, main machine extrusion capacity: 28KG/H (approximately);

4. Coating outer diameter: 0.75mm～Φ5.0mm (max outer diameter of sheath: Φ6.0mm);

5. Flat electromagnetic wire (reserved function): 3.30mm*11.40mm (within the range of 2.0mm*12.0mm), coating thickness: 0.20～0.70mm;